![DMLS Chrome 3D Printing Material](https://proto3000.com/wp-content/uploads/2018/03/Chrome-1-450x500.png)
DMLS Additive Manufacturing Material
Cobalt Chrome MP1
CoCrMo is a Metal Super Allot For High Temperature Engineering and Biomedical Applications
Cobalt Chrome MP1 (CoCrMo) is an additive manufacturing material for a direct metal laser sintering (DMLS) 3D printing process. This class of metal superalloy is designed for biomedical and high-temperature engineering and aerospace applications. Parts 3D printed with Cobalt Chrome are characterized by having excellent mechanical properties, corrosion resistance, and temperature resistance.
Overview
Cobalt Chrome MP1 is a cobalt-chrome-molybdenum-based superalloy that offers designers a metal material which features excellent mechanical properties in terms of strength & hardness plus high corrosion, wear and temperature resistance. This metal is commonly used in biomedical applications (dental & medical implants) as well as high-temperature engineering applications.
Material Performance
Tensile Strength
1350±100 MPa (XY)
1200±150 MPa (Z)
Yield
Strength
1060±100 MPa (XY)
800±100 MPa (Z)
Elongation
at Break
(11±3)% (XY)
(24±4)% (Z)
Material Highlights
Features
- Very high strength
- High temperature & corrosion resistance
- Easily machinable
- Good thermal conductivity
Uses
- High-temperature engineering applications (automotive & aerospace)
- Biomedical applications (medical & dental implants)
Performance Scale
Material Colours
metal
Powered By DMLS
Direct Metal Laser Sintering (DMLS) is a laser-based technology of metal 3D printing that uses powdered metals. 3D printing with metal is the ideal alternative to complex designs that machining or casting can’t achieve as it offers the mechanical properties of aerospace standard materials and the design freedom of additive manufacturing.
Technical Specifications
Properties | As Built | Stress Relieved (at 1150 °C) |
Ultimate Tensile Strength | 1350±100 MPa (XY)
1200±150 MPa (Z) |
1100±100 MPa
|
Yield Strength (Rp 0.2%) | 1060±100 MPa (XY)
800±100 MPa (Z) |
600±50 MPa
|
Elongation at Break | (11±3)% (XY)
(24±4)% (Z) |
20%
|
Modulus of Elasticity | 200±20 GPa (XY)
190±20 GPa (Z) |
200±20 GPa
|
Fatigue Life | 560 MPa (10 mill cycles)
660 MPa (1 mill cycles) |
|
Hardness | 35-45 HRC |